Actividad No 4 1 - luis ramirez

Vista previa del material en texto

U N I V E R S I D A D A U T Ó N O M A D E N U E V O L E Ó N 
 
FACULTAD DE INGENIERÍA MECÁNICA Y ELÉCTRICA 
 
 
 Laboratorio de Mecánica de Materiales 
 
Actividad No.4 
 
Grupo: 407 
 
 
Cd. Universitaria a 12 de abril de 2021 
LM-TASKS 
1902677 Jose Luis Estrada Montoya 
 
http://www.google.com.mx/imgres?q=logo+fime+uanl&um=1&hl=es&sa=N&biw=1600&bih=731&tbm=isch&tbnid=-cnkeT65r8iNwM:&imgrefurl=http://www.fotolog.com/fiime_uanl/41566400/&docid=1b5FuFqNJ4rsAM&imgurl=http://sp7.fotolog.com/photo/55/35/37/fiime_uanl/1259894755095_f.jpg&w=379&h=500&ei=jCpbUPLxD8i9qAHO3YH4Cg&zoom=1&iact=hc&vpx=665&vpy=115&dur=3176&hovh=258&hovw=195&tx=88&ty=151&sig=112200420952746079415&page=1&tbnh=133&tbnw=100&start=0&ndsp=37&ved=1t:429,r:4,s:0,i:80
http://www.google.com.mx/imgres?q=logo+fime+uanl&um=1&hl=es&sa=N&biw=1600&bih=731&tbm=isch&tbnid=t1naWQaneqAQBM:&imgrefurl=http://pisis.fime.uanl.mx/&docid=bRlU1aVNbQrwiM&imgurl=http://pisis.fime.uanl.mx/gifs/logo_uanl.jpg&w=512&h=447&ei=jCpbUPLxD8i9qAHO3YH4Cg&zoom=1&iact=hc&vpx=398&vpy=81&dur=641&hovh=210&hovw=240&tx=100&ty=105&sig=112200420952746079415&page=1&tbnh=133&tbnw=150&start=0&ndsp=37&ved=1t:429,r:2,s:0,i:74
 
Ensayo Estático de Tensión 1 
 
1. Presentación 
Esta empresa está diseñada y a su disposición para realizar cualquier tipo de trabajo mecánico y eléctrico, mantenimiento 
a máquinas y a subestaciones eléctricas. 
El nombre de la empresa está inspirado en mi nombre y apellido junto con la palabra de “Trabajos/tareas” en inglés, ya 
que como lo mencionado estamos capacitados para realizar todo tipo de trabajo antes cotizado. 
El logotipo nos define como empresa, el azul que significa nuestra fidelidad y compromiso que tenemos con el cliente que 
nos quiera contratar para ofrecerle nuestros servicios y el orden que debe de llevar y para dejar en claro nuestro 
compromiso. 
La perica y el martillo cruzados viene siendo representando el tipo de trabajos que podríamos realizar, desde un martillo y 
esta la perica formando una equis “X” demostrando que no hay trabajo que no podamos resolver. 
En esta practica realizaremos una tabla (bitácora) con los datos del ensayo estatico de tensión con el material de Acero 
con su extracción pronunciada y su forma es como un cono cráter, dado esto y los datos que recapitulamos desde la 
actividad pasada y la antepasada que recurrimos también a estos mismos datos (li, lf, Lr, Di, Df, Ai, Af.). 
Para este ensayo se es utilizado para medir la resistencia de un material a una fuerza estática o aplicada lentamente y que 
esto prueba que consiste en alargar una probeta de ensayo por fuerza de tensión, ejercida gradualmente, con el fin de 
conocer ciertas propiedades mecánicas de materiales en general: su resistencia, ductilidad y rigidez. 
En un ensayo de tracción pueden determinarse diversas características de los materiales elásticos, aquí unos ejemplos: 
Módulo de elasticidad o Módulo de Young, que cuantifica la proporcionalidad anterior. Es el resultado de dividir 
la tensión por la deformación unitaria, dentro de la región elástica de un diagrama esfuerzo-deformación. 
 
Coeficiente de Poisson, que cuantifica la razón entre el alargamiento longitudinal y el acortamiento de las 
longitudes transversales a la dirección de la fuerza. 
Límite de proporcionalidad: valor de la tensión por debajo de la cual el alargamiento es proporcional a la carga 
aplicada. 
Límite de fluencia o límite elástico aparente: valor de la tensión que soporta la probeta en el momento de 
producirse el fenómeno de la cedencia o fluencia. Este fenómeno tiene lugar en la zona de transición entre las 
deformaciones elásticas y plásticas y se caracteriza por un rápido incremento de la deformación sin aumento 
apreciable de la carga aplicada. 
Límite elástico (límite elástico convencional o práctico): valor de la tensión a la que se produce un alargamiento 
prefijado de antemano (0,2%, 0,1%, etc.) en función del extensómetro empleado. Es la máxima tensión aplicable 
sin que se produzcan deformaciones permanentes en el material. 
Carga de rotura o resistencia a tracción: carga máxima resistida por la probeta dividida por la sección inicial de la 
probeta. 
Alargamiento de rotura: incremento de longitud que ha sufrido la probeta. Se mide entre dos puntos cuya 
posición está normalizada y se expresa en tanto por ciento. 
Estricción: es la reducción de la sección que se produce en la zona de la rotura. 
 
Jose Luis Estrada Montoya 
 
 
 
2. Bitácora del Ensayo 
Ensayo Estático de Tensión 2 
Estándar: ASTM E8 Descripción de la fractura 
Material: ACERO Estricción: pronunciada 
Li= 100 mm Forma: parcialmente cono cráter 
Lf= 28.5 mm Textura: fina o sedosa 
Lr= 38.1 mm o= 0.006421477 mm/mm 
Di= 10 mm Ai= 78.54 mm2 
Df= 4.38 mm Af= 15.07 mm2 
 
No. Desplazamiento Carga Deformación unitaria Esfuerzo 
Ctvo.  (mm) P (N) (mm/mm) c(mm/mm)  (MPa) 
1 0 0   0 
183 0.558 12560 0.014645669 0.008224192 159.9188868 B 
184 0.562 12680 0.014750656 0.008329179 161.4467743 
261 0.788 21800 0.020682415 0.014260938 277.5662208 
262 0.792 21900 0.020787402 0.014365924 278.8394603 
263 0.796 22100 0.020892388 0.014470911 281.3859394 A 
264 0.799 22200 0.020971129 0.014549651 282.6591789 
265 0.802 22300 0.021049869 0.014628392 283.9324185 
266 0.804 22400 0.021102362 0.014680885 285.205658 
267 0.807 22500 0.021181102 0.014759625 286.4788976 
268 0.81 22600 0.021259843 0.014838365 287.7521371 
269 0.813 22700 0.021338583 0.014917105 289.0253767 
270 0.816 22800 0.021417323 0.014995846 290.2986162 
336 1.012 28600 0.02656168 0.020140203 364.1465098 
337 1.015 28700 0.02664042 0.020218943 365.4197493 
338 1.018 28700 0.02671916 0.020297683 365.4197493 
339 1.021 28800 0.0267979 0.020376423 366.6929889 
340 1.024 28800 0.02687664 0.020455163 366.6929889 
341 1.027 28900 0.026955381 0.020533903 367.9662284 
342 1.029 28900 0.027007874 0.020586397 367.9662284 
343 1.033 29000 0.027112861 0.020691384 369.239468 
344 1.035 29000 0.027165354 0.020743877 369.239468 
345 1.038 29100 0.027244094 0.020822617 370.5127075 
346 1.04 29100 0.027296588 0.020875111 370.5127075 
347 1.043 29200 0.027375328 0.020953851 371.7859471 
348 1.047 29200 0.027480315 0.021058838 371.7859471 
349 1.051 29200 0.027585302 0.021163825 371.7859471 
350 1.054 29300 0.027664042 0.021242565 373.0591866 
351 1.057 29300 0.027742782 0.021321305 373.0591866 
352 1.06 29300 0.027821522 0.021400045 373.0591866 
353 1.062 29400 0.027874016 0.021452539 374.3324262 cedencia 
354 1.066 29400 0.027979003 0.021557525 374.3324262 
355 1.068 29400 0.028031496 0.021610019 374.3324262 
356 1.071 29500 0.028110236 0.021688759 375.6056657 
357 1.075 29500 0.028215223 0.021793746 375.6056657 
358 1.077 29500 0.028267717 0.021846239 375.6056657 
359 1.08 29600 0.028346457 0.02192498 376.8789052 
360 1.082 29600 0.02839895 0.021977473 376.8789052 
361 1.085 29600 0.02847769 0.022056213 376.8789052 
362 1.088 29700 0.02855643 0.022134953 378.1521448 
363 1.09 29700 0.028608924 0.022187447 378.1521448 
364 1.093 29700 0.028687664 0.022266187 378.1521448 
365 1.098 29800 0.028818898 0.02239742 379.4253843 
518 1.55 30800 0.040682415 0.034260938 392.1577798 
519 1.553 30800 0.040761155 0.034339678 392.1577798 
520 1.557 30800 0.040866142 0.034444665 392.1577798 máximo 
521 1.561 30700 0.040971129 0.034549651 390.8845402 
522 1.564 30700 0.041049869 0.034628392 390.8845402 
523 1.566 30700 0.041102362 0.034680885 390.8845402 
524 1.569 30700 0.041181102 0.034759625 390.8845402 
525 1.572 30700 0.041259843 0.034838365 390.8845402 
526 1.575 30700 0.041338583 0.034917105 390.8845402 
544 1.629 30600 0.042755906 0.036334428 389.6113007 
1000 2.98 26100 0.078215223 0.071793746 332.3155212 fractura 
 
 
 
 
0
50
100
150
200
250
300
350
400
450
0 0.01 0.02 0.03 0.04 0.05 0.06 0.07 0.08 0.09
Tí
tu
lo
 d
e
l e
jeTítulo del eje
Series1
 
 
0
50
100
150
200
250
300
350
400
450
0 0.01 0.02 0.03 0.04 0.05 0.06 0.07 0.08
Es
fu
e
rz
o
 (
M
P
a)
Deformación unitaria (mm/mm)
Ensayo Estático de Tensión 2
Series1
Material: acero Estándar: ASTM E8
Li= 100 mm Lf= 28.5 mm
Lr= 38.1 mm
Di= 6.35 mm Df= 4.38 mm
 
 
0
50
100
150
200
250
300
350
400
0 0.005 0.01 0.015 0.02 0.025
Es
fu
e
rz
o
 (
M
P
a)
Deformación unitaria (mm/mm)
Ensayo Estático de Tensión 2
Series2
Material: acero Estándar: ASTM E8
Li= 25.4 mm Lf= 28.5 mm
Lr= 38.1 mm
Di= 6.35 mm Df= 4.38 mm
Resultados del ensayo estático de tensión 2 
1 Estándar ASTM E8 
2 Material ACERO 
3 Longitud recta Lr 38.10 mm 
4 Longitud inicial Li 100.00 mm 
5 Longitud final Lf 28.5 mm 
6 Diámetro inicial Di 10.000 mm 
7 Diámetro final Df 4.380 mm 
8 Área inicial Ai 78.54 mm2 
9 Área final Af 15.067 mm2 
10 Volumen V 2992 mm3 
11 Módulo de Elasticidad (calculado) E 19261 MPa 
12 Módulo de Elasticidad (Tabla) E 200000 MPa 
13 Esfuerzo de cedencia o fluencia y 374.3 MPa 
14 Deformación de cedencia y 0.02145 mm/mm 
15 Carga de cedencia Py 29400 N 
16 Esfuerzo último o máximo u 392.2 MPa 
17 Deformación de esfuerzo máximo u 0.03444 mm/mm 
18 Carga máxima Pu 30800 N 
19 Esfuerzo de fractura f 332.3 MPa 
20 Deformación de fractura f 0.0718 mm/mm 
21 Carga de fractura Pf 26100 N 
22 Dureza (tabla) H 200 HB 
23 Peso especifico  7.681E-05 N/mm3 
24 Resistencia especifica de cedencia Sey 4.873E+06 mm 
25 Resistencia especifica última Seu 5.106E+06 mm 
26 Resiliencia elástica unitaria Reu 4.015 N*mm/mm3 
27 Resiliencia elástica total Ret 12015 N*mm 
28 Tenacidad unitaria Tu 27.51 N*mm/mm3 
29 Tenacidad total Tt 82334 N*mm 
30 Porciento de elongación %  -71.50 % 
31 Porciento de reducción de área %Ra 80.82 % 
32 
Descripción de la fractura 
estricción apreciable 
33 forma 
parcialmente cono 
cráter 
34 textura fina o sedosa